SS 904L Sheets & Plates
The ASME SB625 SS 904L Hot Rolled Plate manufactured by us is harder and stronger and
cannot be heat treated for extra strength but are good for applications like storage
tanks and panels in the pulp and paper industry, acetic acid, sulfuric acid and
phosphoric acid processing plants. Our UNS N08904 Shim Sheet can be used in applications
that use the same material components. Shims are smaller pieces of sheets used to fill
in gaps without compromising the strength and corrosion resistance of the entire
structure. The ASTM B625 Uns N08904 Coil manufactured by us has high corrosion
resistance and strength. These coils could be used in oil refinery components, wiring
and electrostatic precipitators and other structural applications that also require
strength. The WERKSTOFF NR. 1.4539 904L Strip is used in places where larger pieces of
metals cannot be used at the same time the strength and anticorrosive properties have to
be retailed. Our 904L Stainless Steel Cold Rolled Plate is seamless, cold workable,
machinable and supports most forming operations. The plates could be used in corrosive
environments like the seawater applications and marine equipment without corrosion
446 ss possesses good mechanical properties and has excellent corrosion resistance
at very higher temperatures.446 stainless steel is non-hardenable.ASTM A240 Stainless
Steel 446 Forging can be started at 1149°C (2100°F) and completed at 871°C
(1600°F).grade 446 stainless steel hot working is performed in between the ranges 1093-
1177°C (2000-2150° F).grade 446 stainless steel Annealing has to be soaked at 816°C
(1500°F).Type 446 stainless steel is used for oil burners, furnace parts, kiln liners,
heat exchangers, stationary soot blowers in steam boilers and glass molds
Specification
| Dimensions | : | ASTM, ASME and API |
|---|---|---|
| Standard | : | ASTM A240 / ASME SA240 |
| Width | : | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, |
| Thickness | : | 4mm-100mm |
| Length | : | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, |
| Form | : | Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc. |
| Surface Finish | : | 2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, chequered, embossed, hairline, sand blast, Brush, etching, Hot rolled plate (HR), Cold rolled sheet (CR), SATIN (Met with Plastic Coated) etc |
| Hardness | : | Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc |
Material & Grade :
|
Stainless Steel : Grade: 304, 304L, 304H, 309, 309S, 316, 316L, 316H, 310, 310S, 317, 317L, 321, 347, 904L |
Chemical Composition
| Grade | Mn | S | C | Mo | Si | P | N | Cr | Ni |
|---|---|---|---|---|---|---|---|---|---|
| 904l stainless steel plate | 2 max | 0.030 max | 0.035 max | 2.00 – 3.00 | 1.00 max | 0.045 max | 68.89 min | 16.00 – 18.00 | 10.00 – 14.00 |
Mechanical Composition
| Grade | Density | Melting Point | Tensile Strength | Elongation | Yield Strength (0.2%Offset) |
|---|---|---|---|---|---|
| Stainless steel 904L sheet | 8.0 g/cm3 | 1399 °C (2550 °F) | Psi – 75000 , MPa – 515 | 35 % | Psi – 30000 , MPa – 205 |