SS 317/317L Sheets & Plates
The Stainless Steel 317L Sheet and Plate is thus made resistant towards these chemicals and has higher strength at elevated temperatures. As a result, our sheet and plate are having a long life. The Austenitic Stainless Steel 317/317L Sheet Plate is also having the desired quality due to the presence of elements like chromium. These are highly alloy steel sheets and plates having martensitic, ferritic, and austenitic structures. Welding and fabrication of these sheets and plates are easy due to their characteristics. The cold working of the sheet is possible and post-work annealing is done to decrease the internal stress of sheet and plate under working atmospheres. However, the sheet cannot be used or heated at a temperature below 927 degrees Celsius which is 1700 degrees Fahrenheit. Our plates and sheets undergo well-testing for their performance assurance.
Designed as per international and national standards, these UNS S31700, S31703 Sheet & Plate are offered in customized length sizes and shapes to our esteemed clients. Also referred as WNR 1.4449, 1.4438 Sheet & Plate these are available at best possible rates in the market.
Specification
| Dimensions | : | ASTM, ASME and API |
|---|---|---|
| Standard | : | ASTM A240 / ASME SA240 |
| Width | : | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, |
| Thickness | : | 4mm-100mm |
| Length | : | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, |
| Form | : | Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc. |
| Surface Finish | : | 2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, chequered, embossed, hairline, sand blast, Brush, etching, Hot rolled plate (HR), Cold rolled sheet (CR), SATIN (Met with Plastic Coated) etc |
| Hardness | : | Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc |
Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 317 | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18 – 20 | 3 – 4 | 11 – 15 | 57.845 min |
| SS 317L | 0.035 max | 2.0 max | 1.00 max | 0.045 max | 0.030 max | 18 – 20 | 3 – 4 | 11 – 15 | 57.89 min |
Mechanical Composition
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1400 °C (2550 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
Product Usage & Application :
- Usefull in Paper & Pulp Companies
- Usefull in High Pressure Applications
- Usefull in Oil and Gas Industry
- Usefull in Chemical Refinery
- Usefull in Pipeline
- Usefull in High Temperature Application
- Usefull in Water Pipe Line
- Usefull in Nuclear Power Plants
- Usefull in Food Processing and Dairy Industries
- Usefull in Boiler & Heat Exchangers